橡膠低溫脆性試驗機是測出在硫化橡膠和塑料的低溫環(huán)境中沖擊脆化溫度和沖擊脆化臨界溫度的試驗機。試驗片裝載夾具有只裝一組的單組型和可安裝四組的多組型。冷卻方式為壓縮機制冷。

單組型具有4組試料夾具裝置，可以同時安裝20個試驗片。在試料沒在冷凍機里的情況下，只改變刻度盤就可以進行測試。
多組型（型）通過轉(zhuǎn)換卡盤托架底座可以連續(xù)的進行樣品測試，可以節(jié)省樣品放回原處時間，滿足很多樣品各自的測試標準。 

Rubber cryogenic brittleness tester is measured in vulcanized rubber and plastic impact brittle temperature and low temperature environment impact critical temperature embrittlement tester. Test strip loading clamp has only a single set of a set of type and can be installed more groups of four groups. Cooling mode for refrigeration compressor.

A single set of type with 4 groups of sample clamp device, can install 20 test piece at the same time. In the case of sample not in refrigerator, only change the dial can be tested.

More groups of type (type) by transforming the chuck bracket base can be continuous to test sample, can save the time of sample back and meet a lot of samples each test standard.

橡膠低溫脆性試驗機適用標準
JIS K6261 ISO812 （硫化橡膠低溫測試方法-低溫脆化沖擊試驗）
JIS K7216 （塑料低溫脆化測試方法）
JIS K6261、K7216、ASTM-D746、ISO-974
Sample size and shape 樣品尺寸及形狀
按照JIS K6261 ISO812 （硫化橡膠低溫測試方法-低溫脆化沖擊試驗）
JIS K7216 （塑料低溫脆化測試方法）
JIS K6261、K7216、ASTM-D746、ISO-974規(guī)定

橡膠低溫脆化試驗機技術(shù)參數(shù)：
樣品卡盤 ：可以同時夾持5個樣品的夾具（多組型可以同時夾持20個樣品）
沖擊錘速度：1.4—2.4m/sec（可調(diào)） 數(shù)字顯示 0.00m/sec
沖擊錘頂部半徑范圍：1.6±0.1mm
低溫槽：不銹鋼制造（內(nèi)部）
                包含攪拌器
熱介質(zhì)：主要使用乙醇
溫度范圍：-40℃ ～ 20℃
冷卻系統(tǒng)：覆疊壓縮機制冷

溫度上升系統(tǒng)：1.5KW加熱器 
溫度控制系統(tǒng)：數(shù)字溫度控制器 
樣品調(diào)節(jié)計時器：數(shù)字式計時器 
安全裝置：漏電電流斷路器，過熱保護器

主要特點：

卡盤轉(zhuǎn)換部分
在90度角時，4組卡盤能夠安裝徑向形, 當(dāng)旋轉(zhuǎn)手柄時，轉(zhuǎn)換卡盤能夠啟動進入打擊測試狀態(tài)。
樣品打擊狀態(tài)Sample striking position
在規(guī)定的速度下，通過交替打擊錘打擊卡盤里樣品夾中的樣品。
試驗槽（低溫槽）
通過利用雙重的冷動機系統(tǒng)可以冷卻到-70℃。
控制部分
電子電路，設(shè)備依照給定的過程進行程序控制，是機器內(nèi)部固有的

相關(guān)資料

1.GB/T 15256-94 硫化橡膠低溫脆性的測定（多試樣法）
2 GB/T1682-94  硫化橡膠低溫脆性的測定（單試樣法）